The lower calcination temperature compared with other methods can avoid growing and reuniting of powders temperature.

相对其他方法,其煅烧温度低,可以克服因高温煅烧引起的颗粒增大和团聚的缺陷.

互联网摘选

The influence of the calcination temperature on the catalytic activity of o-xylene isomerization was investig.

本文还讨论了焙烧温度对邻二甲苯异构化的催化活性的影响.

互联网摘选

The maxim strength is found when calcination temperature is 600 ℃.

煅烧温度在600℃所制无水石膏水泥强度最大.

互联网摘选

Of pore silica gel, calcination temperature should not exceed 200 ℃.

对细孔硅胶, 焙烧温度不能超过200℃.

互联网摘选

The effects of loading, calcination temperature and calcination time on the solid base catalyst preparation conditions on the yield of dehydroacetic acid.

通过实验考察了负载量、煅烧温度和煅烧时间等固体碱催化剂制备条件对脱氢乙酸产率的影响。

互联网摘选

The change of SO2 partial pressure, O2 partial pressure, average porosity and average pore radius of product layer on unreacted core were discussed based on the model. The features of calcination in constant temperature were also discussed.

在本文所建立模型的基础上讨论了未反应核表面SO2、O2分压的变化，产物层平均孔径和平均孔隙率的变化，并且讨论了实验工况难以实现的恒温煅烧特性。

互联网摘选

The Research On Calcination Temperature and Soaking Time of the Silicon Chrome Green Pigment

硅铬绿色料煅烧温度及保温时间的研究

互联网摘选

The results showed that both the crystalline size and particle size increased with increasing calcination temperature.

检测结果表明，粉体的晶粒度和颗粒度都随煅烧温度的增加而增大。

互联网摘选

The higher the calcination temperature, the larger the crystallite size.

焙烧温度越高，晶粒尺寸越大；

互联网摘选

The effects were reviewed by changing the doping element, doping consent and calcination temperature. Characterizations of micro-structure and UV-vis absorption of modified-TiO2 photocatalyst were analysed using XRD, SEM, UV-vis.

通过改变掺杂元素、掺杂量和焙烧温度等考察对TiO2光催性的影响，同时利用XRD、SEM、UV-Vis等分析手段，表征了改性TiO2光催化剂微观结构和光吸收能力。

互联网摘选

The effects of the preparation conditions, such as calcination temperature, ratio of sol and zeolite and exchange times were investigated.

研究了煅烧温度，溶胶沸石配比，交换次数等制备条件对催化剂的影响。

互联网摘选

Studies on the mechanism of leaching silicon and aluminum from bentonite have been processed by adjusting reaction time, calcination temperature, ratio of alkali to bentonite, the kind of alkali etc.

并通过改变反应时间、煅烧温度、碱土比、碱的种类、以及焙烧与否，对膨润土的硅、铝浸出机理作了比较深入的研究。

互联网摘选

The synthesis conditions were investigated such as the type of template, calcination temperature, molar ratio of water and titanium source, and molar ratio of template and titanium source.

通过改变模板剂的类型、焙烧温度、水和钛源的摩尔比、模板剂和钛源的摩尔比等因素，探索制备有序介孔二氧化钛的最佳条件。

互联网摘选

The optimal reaction conditions were determined: the concentration of hydrochloric acid was 3%, boiling time was 4 h, calcination temperature was 550 ℃.

对新方法制备白炭黑的工艺条件进行了研究，确定了反应的最佳工艺条件：盐酸质量分数为3%，煮沸时间为4h，煅烧温度为550℃。

互联网摘选